creep fracture

基本解釋

The improvement factors for creep fracture strength were discussed.
討論了稀土元素改善耐熱鋼熱強(qiáng)性的因素。
Work condition and force acting of the bolt were analyzed. The bolt failure was creep fracture mainly due to their high temperature work condition.
經(jīng)過對螺栓的服役條件以及工作中受力情況進(jìn)行分析，認(rèn)為螺栓斷裂主要是由于長時間在高溫條件下發(fā)生蠕變導(dǎo)致的。
However, the creep fracture of medium strength match joint, located in the low strength base metal remote from the weld interface, showed a ductile fracture character.
中強(qiáng)匹配接頭蠕變斷裂位置在遠(yuǎn)離焊縫界面的低強(qiáng)度母材區(qū)，呈延性斷裂性質(zhì)。