intergranular stress corrosion

基本解釋

The exfoliation of alloy happens from original pitting to intergranular corrosion and with cooperation of stress.
研究表明，合金的剝蝕是一個從點蝕發(fā)展到晶間腐蝕，然后在應力協(xié)同作用下發(fā)生破壞的過程。
The cracking of alloy with very low stress-corrosion resistance, welded and stored in open air for a long time, is caused by the welded stress and such a fracture is a typical intergranular fracture.
抗應力腐蝕性能低的合金焊接后，在大氣中長期存放沿熔合線發(fā)生的開裂，是由焊接應力引起的，斷口是典型的脆性沿晶斷裂。
The corrosion behavior of 2D12 alloy was evaluated including intergranular corrosion, exfoliation and stress corrosion cracking.
對不同規(guī)格2D12鋁合金進行晶間腐蝕、剝蝕和應力腐蝕性能測定。