theoretical density

基本解釋

The relationships between the theoretical density and porosity of the composites and the repetition cycle are discovered.
從理論上揭示了復(fù)合材料的浸漬-裂解周期與材料的理論密度和理論孔隙率之間的關(guān)系。
A case study on SLS of this Cu-based metal powder to fabricate a gear is carried out. 82% relative theoretical density and transverse dimension error of 1.9% are achieved.
最后給出了激光燒結(jié)上述金屬粉末制造齒輪的加工實例，其致密度達理論密度的82%，而橫向尺寸誤差僅為1.9%。
The technology of repressing and re-sintering in powder metallurgy had been used to fabricate a(c)Cu-C) composite materials attaining above 95% of the theoretical density.
采用粉末冶金復(fù)壓復(fù)燒技術(shù)制備出高密度的銅碳復(fù)合材料，對兩種成分銅碳復(fù)合材料的顯微組織、物理力學(xué)性能和耐磨性能進行了對比試驗。