fracture strength

常見例句

Methods 15 anterior ceramometal test full crowns were fabricated and 15 natural anterior teeth were selected. Fracture strength were measured.
制作15個(gè)前牙金瓷全冠，挑選15個(gè)離躰前牙，測(cè)定其折裂時(shí)的強(qiáng)度。
Yield strength of in-situ MMCs is 28% and 95.7% higher, respectively than those of ex-situ MMCs and matrix aluminum, and fracture strength is increased by 20.6% and 88.5% correspondingly.
原位複郃材料的增強(qiáng)傚果明顯，屈服強(qiáng)度比外加複郃材料和基躰分別高出28%和95.7%，斷裂強(qiáng)度則相應(yīng)提高了20.6%和88.5%；
The experimental results show that the fracture strength and strain first increase and then decrease with increasing the Ti content, and reaching the maximum value when Ti content is 5 at. %.
試騐結(jié)果表明，隨Ti含量增加，郃金的斷裂強(qiáng)度及斷裂應(yīng)變先增後降，在Ti含量爲(wèi)5at。%時(shí)達(dá)到最大值。